E71T-1 Use is CO2 flux cored wire for welding titanium
- Detail
E501T-1, E71T-1
Use is CO2 flux cored wire for welding titanium. High deposition efficiency, excellent all-position welding performance can also be vertical down welding. For ships, pressure vessels, mechanical equipment, steel bridges, steel low carbon steel and 490MPa grade high strength steel welding. Standard:
GB / T: E501T-1
AWS: E71T-1
| Package | Package | Silk panel | Net weight |
| Φ1.0~1.6(mm) | D100mm D200mm D270mm D300mm K300mm | 1 kg, 5 kg, 15 kg18 kg, 20 kg |
| Chemical (%) | C | Mn | Si | P | S | ||||
| ≤0.10 | ≤1.75 | ≤0.75 | ≤0.03 | ≤0.03 | |||||
| Deposited metal Mechanical properties | Yield strengthσ0.2(Mpa) | Tensile strengthσb(Mpa) | Elongationδ5(%) | AKV Impact Energy(J) | |||||
| ≥400 | ≥480 | ≥22 | ≥47(0℃) |
≥47(-20℃) |
|||||
| Wire diameter(mm) | Φ1.0 | φ1.2 | φ1.4 | φ1.6 | Welding position |  |
| Welding current(AMP.) | 80~250 | 120~300 | 160~400 | 190~450 | ||
| Notes: | 1 wire into the plant must be stored in a dry environment, not just open the disk waterproof wire welding package 2 should be removed before welding surface of the oil, rust, moisture and other impurities 3. The use of CO2 gas, CO2 gas purity of 99.98%. 4 CO2 protection welding gas flow should be controlled in 20-25L/min. 5 out of wire length should be controlled at 15-25mm range. 6 to be preheated before welding to 150-300 ℃, after welding to be tempered by 700-740 ℃. |
|||||
We support OEM production, so we can purchase materials according to your needs to achieve more suitable prices.
We have a very strict test system, and the product yield is 95%. GB50-6 is our QC standard.